ISO 3387-2020 pdf free.Rubber — Determination of crystallization effects by hardnessmeasurements.
This document specifies a test based on hardness measurements for determining the progressivestiffening of rubber with time, caused by crystallization. It is limited to materials having an initialhardness at a test temperature of from 10 IRHD to 85 IRHD.
The method is applicable to raw, unvulcanized (compounded) and vulcanized rubber. It is mainly ofinterest for rubber with a marked crystallization tendency at temperatures experienced in coldclimates, such as chloroprene and natural rubber.
The method is not applicable to fast-crystallizing materials which crystallize to a considerable degreewithin the timespan of 15 min used for conditioning at test temperature.
The following documents are referred to in the text in such a way that some or all of their contentconstitutes requirements of this document. For dated references,only the edition cited applies. Forundated references, the latest edition of the referenced document (including any amendments) applies.ISO 48-2:2018,Rubber,vulcanized or thermoplastic – Determination of hardness — Part 2: Hardnessbetween 10 IRHD and 100 IRHD
ISO 18899:2013, Rubber — Guide to the calibration of test equipment
ISO23529,Rubber —General procedures for preparing and conditioning test pieces for physical test methods
All final handling and measurements shall be made within the cold chamber while the test temperatureremains within the permissible limits.This can be done by providing suitable equipment which permitsmanipulation of materials within the chamber from the outside (for example, by means of handholesand gloves through the door or wall of the cabinet).
Hardness gauges, in accordance with IS0 48-2.Lubricants, if used, shall be of a type not causingfriction in the instrument at the test temperature.The hardness gauge used in this test procedure is normally conditioned and operated inside the coldchamber. Alternatively, a special device may be used where the body of the hardness gauge is placedoutside the cold chamber and connected with the indenter in the cold chamber by means of a rod withlow heat-conductive capacity, and constructed to avoid the introduction of additional friction.ISO 3387 pdf download.

Download infomation Go to download
Note: Can you help me share this website on your Facebook or others? Many thanks!
AS ISO ASTM 52904:2021 pdf free Free AS Standards

AS ISO ASTM 52904:2021 pdf free

AS ISO ASTM 52904:2021 pdf free.Additive manufacturing - Process characteristics and performance - Practice for metal powder bed fusion process to meet critical applications. 5 Feedstock and Powder Batches 5.1 The material supplier shall package the powder...
Get More
AS ISO/ASTM 52901:2021 pdf free Free AS Standards

AS ISO/ASTM 52901:2021 pdf free

AS ISO ASTM 52901:2021 pdf free.Additive manufacturing - General principles - Requirements for purchased AM parts. 4.3.3 Tolerances The tolerances shall be specified (e.g. general tolerances, see ISO 2768-1 and ISO 2768-2, and/or specific, ISO 1101), including...
Get More
AS ISO 16809:2020 pdf free Free AS Standards

AS ISO 16809:2020 pdf free

AS ISO 16809:2020 pdf free.Non-destructive testing — Ultrasonic thickness measurement. 5 General requirements 5.1 Instruments The following types of instruments shall be used to achieve thickness measurement: a) dedicated ultrasonic thickness measurement instruments with numerical display showing...
Get More


Anonymous netizen Fill in information