IEC 60754-2-2019 pdf free.Test on gases evolved during combustion of materials from cables – Part 2: Determination of acidity (by pH measurement) and conductivity.
This part of IEC 60754 specifies the apparatus and procedure for the determination of the potential corrosivity of gases evolved during the combustion of materials taken from electric or optical fibre cable constructions by measuring the acidity (pH) and conductivity of an aqueous solution resulting from the gases evolved during the combustion. The heating (combustion) procedure of this part of IEC 60754 is the same as in IEC 60754-3.
The general method specified in this standard is intended for the testing of individual components used in a cable construction. Formulae are given for the calculation of a weighted value for a combination of materials found in a specified cable. The use of this method will enable the verification of relevant requirements for either individual components or combined components of a cable construction stated in the appropriate cable specification.
A simplified method is included for the testing of individual components where it is required only to demonstrate compliance with a stated performance requirement for quality control purposes.
NOTE 1 The relevant cable standard should Indicate which components of the cable should be tested, and which method of calculation (see Clause 8) should be used in the case of dispute
NOTE 2 This test method may be used to test materials to be used in cable manufacture, but a declaration of cable performance should not be made based on such a test.
NOTE 3 For the purposes of this standard, the term -electric cable covers all insulated metallic conductor cables used for the conveyance of energy or signals.
2 Normative references
The following referenced documents are indispensable for the application of this document. For dated references, only the edition cited applies. For undated references, the latest edition of the referenced document (including any amendments) applies.
ISO 1042, Laboratory glassware — One-mark volumetric flasks
(available only in French)
ISO 3696, Water for analytical laboratory use — Specification and test methods
3 Terms and definitions
For the purposes of this document, the following terms and definitions apply.
4 Test method principle
The material under test shall be heated in a stream of dry air. The evolved gases shall be trapped by bubbling through wash bottles filled with distilled or demineralized water.
The acidity of the resulting solution shall be assessed by determination of its pH value. The conductivity of the solution shall also be determined.
5 Test apparatus
5.1 General
The apparatus is shown in Figures 1 to 5.
The assembly of the components which constitute the test apparatus shall be leak-tight. The connecting distances between the quartz glass tube and the first bottle and between subsequent bottles shall be as short as possible. Glass or silicone rubber tubing shall be used for these connections.
NOTE 1 At the exit side of the quartz glass tube, as close to the end as possible, it is permitted to place a plug of silica wool to aid collection of condensates.
NOTE 2 A third empty bottle, of the same size as the gas washing bottles, placed before the gas washing bottles may be used to improve safety. i.e. to prevent suck back of water into the quartz glass tube.
5.2 Tube furnace
The length of the heating zone of the furnace shall be within the range 480 mm to 620 mm and its inside diameter shall be within the range 38 mm to 62 mm. It shall be equipped with an adjustable electrical heating system.
5.3 Quartz glass tube
For the test, a quartz glass tube shall be introduced into the tube furnace. The tube shall be approximately concentric to the furnace. It shall be resistant to the action of corrosive gases.
The inside diameter of the tube shall be within the range 30 mm to 46 mm. The tube shall protrude on the entrance side of the furnace by a length of between 60 mm to 200 mm. and on the exit side by between 60 mm to 100 mm. The initial clearance shall allow for thermal expansion. For the purposes of measurement of the protrusion distances, the tube shall be regarded as that part of essentially constant diameter.IEC 60754-2 pdf download.