ISO 15854-2021 pdf free.Dentistry – Casting and baseplate waxes.
5.6 Behaviour on softening (Type 2)
The wax shall soften without becoming sticky or crumbly and shall be mouldable without breaking or delaminating when tested in accordance with $.
This requirement shall not apply to baseplate preforms where a suitable square test piece cannot be cut.
5.7 Residue on artificial teeth (Type 2)
The wax shall not leave a visible residue on either ceramic or synthetic polymer teeth when tested in accordance with J.
5.8 Behaviour of colouring material (Type 2)
The colouring material shall neither separate from the wax nor impregnate the gypsum mould when tested in accordance with 1L7.
5.9 Adhesion on storage (Type 2)
Adhesion due to storage of the wax shall be such that, when tested in accordance with there shall be no evidence of damage to wax surfaces. Wax and separating paper surfaces shall separate cleanly and readily.
NOTE The separating paper might not cover the whole area of the wax sheet.
5.10 Residue on ignition (Type 1)
lithe manufacturer does not state a value for the residue on ignition, the value as determined in accordance with 9 shall be no greater than 0,10 % by mass.
lithe residue on ignition is greater than 0,10 % by mass, this value shall be stated by the manufacturer and the value as determined in accordance with 89 shall be not more than 20 % greater than that stated value.
5.11 Biocompatibility
See ISO 7405 and ISO 10993-1 for guidance on compatibility in respect of waxes that are offered for use
in the mouth or that are not specifically excluded from that application.
6 Sampling
The amount of material procured for testing shall be at least 250 g for Type 1, or 500 g for Type 2, and from one batch, and one packet where possible. This material shall be obtained on the open market unannounced and thus taken randomly from stock.
7 Test methods — General
7.1 Ambient temperature
Unless otherwise specified in this document, all test piece preparation and testing shall be conducted at an ambient temperature of (23 ± 2) °C. Where necessary and appropriate, all material shall be allowed to eqLlilibrate at this ambient temperature before testing for at least 24 h.ISO 15854 pdf download.

Download infomation Go to download
Note: Can you help me share this website on your Facebook or others? Many thanks!
AS ISO ASTM 52904:2021 pdf free Free AS Standards

AS ISO ASTM 52904:2021 pdf free

AS ISO ASTM 52904:2021 pdf free.Additive manufacturing - Process characteristics and performance - Practice for metal powder bed fusion process to meet critical applications. 5 Feedstock and Powder Batches 5.1 The material supplier shall package the powder...
Get More
AS ISO/ASTM 52901:2021 pdf free Free AS Standards

AS ISO/ASTM 52901:2021 pdf free

AS ISO ASTM 52901:2021 pdf free.Additive manufacturing - General principles - Requirements for purchased AM parts. 4.3.3 Tolerances The tolerances shall be specified (e.g. general tolerances, see ISO 2768-1 and ISO 2768-2, and/or specific, ISO 1101), including...
Get More
AS ISO 16809:2020 pdf free Free AS Standards

AS ISO 16809:2020 pdf free

AS ISO 16809:2020 pdf free.Non-destructive testing — Ultrasonic thickness measurement. 5 General requirements 5.1 Instruments The following types of instruments shall be used to achieve thickness measurement: a) dedicated ultrasonic thickness measurement instruments with numerical display showing...
Get More


Anonymous netizen Fill in information